Abrégé

5050) of 100-900 nm. The α-alumina particles are produced in such a way that pseudobohemite is mixed with a fluoride-based mineralizer and ultrapure water and pulverized to obtain a powder which is then fired and grown into a polyhedral shape. The polyhedral alumina particles make surface contact and are coated on the surface of a porous polymer substrate, and empty space induced by the interstitial volume between particles is formed larger than that of spherical particles, thereby being capable of achieving excellent air permeability while effectively suppressing thermal contraction of the porous polymer substrate. In addition, due to a nano-level particle size, excellent dispersibility and the formation of a thin coating layer can be achieved.

Classes IPC  ?

• C09D 5/00 - Compositions de revêtement, p.ex. peintures, vernis ou vernis-laques, caractérisées par leur nature physique ou par les effets produits; Apprêts en pâte
• C01F 7/441 - Déshydratation de l’oxyde ou de l'hydroxyde d'aluminium, c. à d. toutes les conversions d'une forme en une autre impliquant une perte d’eau par calcination
• C01F 7/021 - Post-traitement des oxydes ou des hydroxydes
• H01M 50/434 - Céramiques
• H01M 50/446 - Matériau composite constitué d’un mélange de matériaux organiques et inorganiques
• H01M 50/449 - Séparateurs, membranes ou diaphragmes caractérisés par le matériau ayant une structure en couches
• H01M 50/489 - Séparateurs, membranes, diaphragmes ou éléments d’espacement dans les cellules caractérisés par leurs propriétés physiques, p.ex. degré de gonflement, hydrophilicité ou propriétés pour court-circuiter
• C09D 1/00 - Compositions de revêtement, p.ex. peintures, vernis ou vernis-laques, à base de substances inorganiques
• C09D 7/00 - Caractéristiques de compositions de revêtement non prévues dans le groupe ; Procédés pour l’incorporation d’ingrédients dans des compositions de revêtement

Abrégé

The present invention provides a method for manufacturing plate type α-alumina particles, plate type α-alumina particles produced therefrom, and a pearlescent pigment comprising same, the method comprising the steps of: (S1) adding pseudoboehmite, molten salt, and additives to a dispersion medium, and mixing, drying, and pulverizing same; (S2) heating dried powder obtained after pulverization in step (S1) to 800-900℃ at a temperature increase rate of 2-3℃/min, and then maintaining same for 4-8 hours to generate seeds; and (S3) heating the seeds produced in step (S2) to 1,000-1,300℃ at a temperature increase rate of 3-5℃/min and then maintaining same for 4 to 6 hours to grow crystals. According to the present invention, it is possible to manufacture plate type α-alumina that can be effectively used as a pearlescent pigment by exhibiting a narrow particle size distribution through the use of pseudoboehmite as a raw material and heat treatment according to stepwise calcination.

Classes IPC  ?

• C01F 7/02 - Oxyde d'aluminium; Hydroxyde d'aluminium; Aluminates
• C30B 1/02 - Croissance des monocristaux à partir de l'état solide par traitement thermique, p.ex. recuit sous contrainte
• C30B 29/16 - Oxydes
• C09C 1/40 - Composés de l'aluminium

Abrégé

The present invention provides an abrasive comprising α-alumina particles having a polyhedral crystal structure, wherein the α-alumina particles have an average diameter (D50) of 300 nm to 10 μm and a bulk density of 0.2-0.5 g/mL, a [0001] face in the crystal structure of the α-alumina particles occupies 10-20% on the basis of the total crystal face area, and the amount of α-alumina particles is 85-100 wt% on the basis of the total weight. The abrasive of the present invention comprises α-alumina particles satisfying predetermined particle size and density ranges while having a polyhedral crystal structure, and thus provides excellent dispersibility in a polishing slurry to enable a polishing rate to increase, while minimizing scratch formation during polishing.

Classes IPC  ?

• C09K 3/14 - Substances antidérapantes; Abrasifs
• B24B 57/02 - Dispositifs pour l'alimentation, l'application, le triage ou la récupération de produits de meulage, polissage ou rodage pour l'alimentation en produits de meulage, polissage ou rodage à l'état fluide, vaporisés, pulvérisés ou liquéfiés
• B24B 49/00 - Appareillage de mesure ou de calibrage pour la commande du mouvement d'avance de l'outil de meulage ou de la pièce à meuler; Agencements de l'appareillage d'indication ou de mesure, p.ex. pour indiquer le début de l'opération de meulage