Abrégé

A continuous electrophoretic deposition modified carbon fiber reinforced multi-matrix composite material, composed of 30-55% by volume fraction of carbon fiber, 3-25% by volume fraction of inorganic powder, and 20-67% by volume fraction of a matrix, the inorganic powder being wrapped on the surface of the carbon fiber or being embedded in a carbon fiber bundle, and the concentration being gradually reduced from a fiber filament to the surface of the fiber bundle. A preparation method for the continuous electrophoretic deposition modified carbon fiber reinforced multi-matrix composite material comprise the steps of: pretreating carbon fiber; preparing slurry of inorganic powder; widening the pretreated carbon fiber to form a carbon fiber strip, and then performing electrophoretic deposition on the inorganic powder; preparing a preform from the deposited carbon fiber; and compounding a matrix in the preform. Uniform deposition of the inorganic powder on the surface of the carbon fiber filament is guaranteed by widening treatment of the carbon fiber, the deposition efficiency is improved, and the performance and the stability of the composite material are improved.

Classes IPC  ?

• C04B 35/571 - Céramiques fines obtenues à partir de précurseurs polymères
• C04B 35/577 - Composites
• C04B 35/622 - Procédés de mise en formeTraitement de poudres de composés inorganiques préalablement à la fabrication de produits céramiques
• C04B 35/628 - Revêtement des poudres
• C08J 5/06 - Renforcement des composés macromoléculaires avec des matériaux fibreux en vrac ou en nappes utilisant des matériaux fibreux prétraités
• C08J 5/24 - Imprégnation de matériaux avec des prépolymères pouvant être polymérisés en place, p. ex. fabrication des "prepregs"
• C08L 63/00 - Compositions contenant des résines époxyCompositions contenant des dérivés des résines époxy
• C08K 9/10 - Ingrédients encapsulés
• C08K 7/06 - Éléments
• C22C 47/12 - Imprégnation ou coulée sous une pression mécanique
• C22C 47/04 - Prétraitement des fibres ou des filaments par revêtement, p. ex. avec un recouvrement protecteur ou activé
• C22C 49/06 - Aluminium
• C22C 49/14 - Alliages contenant des fibres ou des filaments métalliques ou non métalliques caractérisés par les fibres ou les filaments
• C25D 13/16 - FilsBandesFeuilles
• C25D 13/02 - Revêtement électrophorétique caractérisé par le procédé avec des matières inorganiques
• C22C 121/02 - Fibres ou filaments revêtus, p. ex. fibres céramiques avec des revêtements protecteurs
• C22C 101/10 - Carbone

Abrégé

The present disclosure discloses a continuous electrophoretic deposition modified carbon fiber reinforced multi-matrix composite and a preparation method thereof, composing of a carbon fiber with a volume fraction of 30-55%, an inorganic powder with a volume fraction of 3-25% and a matrix with a volume fraction of 20-67%, wherein the inorganic powder is wrapped on the surface of the carbon fiber filament or embedded in the carbon fiber bundle, and the concentration gradually decreases from the fiber filament to the surface of the fiber bundle. The preparation method of the composite is as follows: (1) pretreating the carbon fibers; (2) preparing a slurry of the inorganic powder; (3) widening the pretreated carbon fiber to form a carbon fiber strip, and then carrying out electrophoretic deposition on the inorganic powders; (4) preparing a preform from the deposited carbon fibers; and (5) compounding a matrix in the preform.

Classes IPC  ?

• C04B 35/80 - Fibres, filaments, "whiskers", paillettes ou analogues
• C04B 35/628 - Revêtement des poudres
• C04B 35/64 - Procédés de cuisson ou de frittage
• C08J 5/24 - Imprégnation de matériaux avec des prépolymères pouvant être polymérisés en place, p. ex. fabrication des "prepregs"
• C25D 13/02 - Revêtement électrophorétique caractérisé par le procédé avec des matières inorganiques
• C25D 13/16 - FilsBandesFeuilles
• C25D 13/20 - Prétraitement
• C22C 49/14 - Alliages contenant des fibres ou des filaments métalliques ou non métalliques caractérisés par les fibres ou les filaments
• C22C 49/06 - Aluminium
• C22C 47/08 - Fabrication d'alliages contenant des fibres ou des filaments métalliques ou non métalliques par mise en contact des fibres ou des filaments avec un métal fondu, p. ex. en imprégnant les fibres ou les filaments placés dans un moule
• C22C 47/04 - Prétraitement des fibres ou des filaments par revêtement, p. ex. avec un recouvrement protecteur ou activé